Viewed 3346 Times Published:2010-9-1 Factors Affecting Concrete Strength

Factors Affecting Concrete Strength


There are many relevant factors; some of the more important follow:
Concrete porosity: voids in concrete can be filled with air or with water. Air voids are an obvious and easily-visible example of pores in concrete. Broadly speaking, the more porous the concrete, the weaker it will be. Probably the most important source of porosity in concrete is the ratio of water to cement in the mix, known as the 'water to cement' ratio. This parameter is so important it will be discussed separately below.

Water/cement ratio: this is defined as the mass of water divided by the mass of cement in a mix. For example, a concrete mix containing 400 kg cement and 240 litres (=240 kg) of water will have a water/cement ratio of 240/400=0.6. The water/cement ratio may be abbreviated to 'w/c ratio' or just 'w/c'. In mixes where the w/c is greater than approximately 0.4, all the cement can, in theory, react with water to form cement hydration products. At higher w/c ratios it follows that the space occupied by the additional water above w/c=0.4 will remain as pore space filled with water, or with air if the concrete dries out.

Consequently, as the w/c ratio increases, the porosity of the cement paste in the concrete also increases. As the porosity increases, the compressive strength of the concrete will decrease.

Soundness of aggregate: it will be obvious that if the aggregate in concrete is weak, the concrete will also be weak. Rocks with low intrinsic strength, such as chalk, are clearly unsuitable for use as aggregate.

Aggregate-paste bond: the integrity of the bond between the paste and the aggregate is critical. If there is no bond, the aggregate effectively represents a void; as discussed above, voids are a source of weakness in concrete.

Cement-related parameters: many parameters relating to the composition of the individual cement minerals and their proportions in the cement can affect the rate of strength growth and the final strength achieved. These include:

alite content

alite and belite reactivity

cement sulfate content

Since alite is the most reactive cement mineral that contributes significantly to concrete strength, more alite should give better early strengths ('early' in this context means up to about 7 days). However, this statement needs to be heavily qualified as much depends on burning conditions in the kiln. It is possible that lighter burning of a particular clinker could result in higher early strength due the formation of more reactive alite, even if there is a little less of it. Not all alite is created equal!

For a particular cement, there will be what is called an 'optimum sulfate content,' or 'optimum gypsum content.' Sulfate in cement, both the clinker sulfate and added gypsum, retards the hydration of the aluminate phase. If there is insufficient sulfate, a flash set may occur; conversely, too much sulfate can cause false-setting.

A balance is therefore required between the ability of the main clinker minerals, particularly the aluminate phase, to react with sulfates in the early stages after mixing and the ability of the cement to supply the sulfate. The optimum sulfate content will be affected by many factors, including aluminate content, aluminate crystal size, aluminate reactivity, solubilities of the different sources of sulfate, sulfate particle sizes and whether admixtures are used.

If this were not already complicated enough, the amount of sulfate necessary to optimize one property, strength for example, may not be the same as that required to optimize other properties such as drying shrinkage. Concrete and mortar may also have different optimum sulfate contents.

This fascinating area is discussed further under ' cement-related concrete strength variability .'

In addition to the compositional parameters considered above, physical parameters are also important, particularly cement surface area and particle size distribution.

The fineness to which the cement is ground will evidently affect the rate at which the cement hydrates; grinding the cement more finely will result in a faster reaction. Fineness is often expressed in terms of total particle surface area, eg: 400 square metres per kilogram. However, of as much, if not more, importance is the particle size distribution of the cement; relying simply on surface area measurements can be misleading. Some minerals, gypsum for example, can grind preferentially producing a cement with a high surface area. Such a cement may contain very finely-ground gypsum but also relatively coarse clinker particles resulting in slower hydration